No edit summary |
|||
Line 18: | Line 18: | ||
==Build Instructions== | ==Build Instructions== | ||
== | ==Testing with Athena RepRap 3D printer== | ||
===10/23/15 - Test 0=== | ===10/23/15 - Test 0=== | ||
[[File:Athena_max333605_test0.JPG|thumb|left|Maxpower 333605 print result.]] | [[File:Athena_max333605_test0.JPG|thumb|left|Maxpower 333605 print result.]] | ||
Line 29: | Line 29: | ||
*Temperature: 260 C | *Temperature: 260 C | ||
*Print speed: Variable (testing capabilities) | *Print speed: Variable (testing capabilities) | ||
*Slicing: Cura 15.04 set to 3mm filament, 1 multiplier, 0.2mm layer height, 70mm/s, 25% infill, 30mm/s initial layer speed | *Slicing: Cura 15.04 set to 3mm filament, 1 multiplier, 0.2mm layer height, print speed 70mm/s, 25% infill, 30mm/s initial layer speed | ||
*Bed: | *Bed: Mirror with glue stick | ||
{{clear}} | {{clear}} | ||
====Notes==== | ====Notes==== | ||
#First layer too close to glass requiring decrease in speed. | #First layer too close to glass requiring decrease in speed. | ||
#Using a 12V fan on the end effector with pwm. Fan speed too high, end effector would not reach target temperature. Occluded lower half of fan with masking tape. | #Using a 12V fan on the end effector with pwm. Fan speed too high, end effector would not reach target temperature. Occluded lower half of fan with masking tape. | ||
#Adjusted speed | #Adjusted speed from 30% (21mm/s) to 140% (98mm/s) in 10% increments (70mm/s speed set in slicing) while printing first ~100 layers. | ||
#Lower layers exhibited poor interlayer bonding | #Lower layers exhibited poor interlayer bonding. | ||
#Resulting print is flexible, but makes cracking noise when squeezed due to poor interlayer bonding | #Resulting print is flexible, but makes cracking noise when squeezed due to poor interlayer bonding. | ||
#Experienced minor respiratory irritation during test. Future tests will be conducted under a hood. | |||
==See also== | ==See also== |
Revision as of 12:53, 23 October 2015
BOM
- Lulzbot hexagon hotend $70 https://www.lulzbot.com/products/lulzbot-hexagon-hot-end
- 24V/4-5A power supply
- 3mm id x 6mm od PTFE tubing 630mm long
- 2x M6 x 0.8mm hex nut
- 3mm print effector
- 3mm extruder drive body
- ~1m 18ga speaker wire
- 2x ~1m 28ga twisted pair
- Heat shrink tubing
OpenSCAD design
- End effector - download latest version of [Athena SCAD files] and [SCAD libraries]. Change the Bowden dimensions in athena.scad. Render the end effector and print.
- Extruder drive - download latest version of [extruder drive SCAD files] (requires the SCAD library, as above). Change the filament dimensions in extruder_drive_renderer.scad. Render the extruder drive body and print.
Build Instructions
Testing with Athena RepRap 3D printer
10/23/15 - Test 0
Conditions
- Filament: Maxpower 333605 Residential Grade Round .105-Inch Trimmer Line 690-Foot Length from Amazon for $24.35/3 pounds (1.3kg $18.73/kg)
- End effector: 3mm Athena print effector
- Hot end: Lulzbot Hexagon, 3mm x 0.35mm
- Extruder drive: 3mm Phidias extruder drive
- Firmware: Franklin (latest)
- Temperature: 260 C
- Print speed: Variable (testing capabilities)
- Slicing: Cura 15.04 set to 3mm filament, 1 multiplier, 0.2mm layer height, print speed 70mm/s, 25% infill, 30mm/s initial layer speed
- Bed: Mirror with glue stick
Notes
- First layer too close to glass requiring decrease in speed.
- Using a 12V fan on the end effector with pwm. Fan speed too high, end effector would not reach target temperature. Occluded lower half of fan with masking tape.
- Adjusted speed from 30% (21mm/s) to 140% (98mm/s) in 10% increments (70mm/s speed set in slicing) while printing first ~100 layers.
- Lower layers exhibited poor interlayer bonding.
- Resulting print is flexible, but makes cracking noise when squeezed due to poor interlayer bonding.
- Experienced minor respiratory irritation during test. Future tests will be conducted under a hood.