===Cutting, Polishing, and Etching===
===Cutting, Polishing, and Etching===
The bulk crystals (boule) has is generally cylindrical with conical ends, which are usually cut off and wasted because their diameter isn't big enough to be used.  Next, the boule is ground to ensure a uniform diameter over the length of the boule which is usually done with a lathe, or similar tool.  The crystals need to be aligned using x-ray diffraction and then the boule is cut into wafers.  <ref name="[2]"> </ref>
The bulk crystals (boule) has is generally cylindrical with conical ends, which are usually cut off and wasted because their diameter isn't big enough to be used.  Next, the boule is ground to ensure a uniform diameter over the length of the boule which is usually done with a lathe, or similar tool.  The crystals need to be aligned using x-ray diffraction and then the boule is cut into wafers.  In this process nearly one third of the total mass can be lost due to the width of the cutting mechanism. <ref name="[2]"> </ref>  The sawing also leaves a damaged layer of semiconductor which is etched off.
The final step in processing the semiconductor is polishing.  There are two different types of waste that are produced during polishing, liquid and solid wastes.  The wastewater from GaAs polishing can contain arsenic and gallium waste in concentrations between 200 and 400 ppm. <ref name="[2]"></ref>


==Thin Film Growth==
==Thin Film Growth==

Revision as of 21:24, 4 October 2011

Template:MY3701


Introduction

Gallium arsenide (GaAs) is a semiconductor material that is used in a wide variety of applications ranging from circuits to solar cells. Solar cell of GaAs can be produced using both bulk and thin film growth methods.

Material Processing

Manufacturing process of GaAs and other semiconductors with the waste products produced

Bulk Growth

There are two common ways to produce GaAs using bulk growth, Liquid-Encapsulated Czochralski (LEC) growth, and Vertical Gradient Freeze (VGF) technology. [1]

LEC growth is accomplished by melting high-purity arsenic and gallium in a high temperature vessel, and slowly cooling to produce a single crystal. The GaAs crystal produced using this method however has some impurities such as significant levels of carbon, and numerous dislocations. These impurities cause the semiconductor to be unusable for some applications.

VGF growth works by placing high purity arsenic and gallium in an enclosed quartz ampoule with a crystal of GaAs. The arsenic and gallium are melted, and then brought into contact with the GaAs crystal. When cooled slowly, a single crystal of GaAs is formed. The single crystal formed has many of the same impurities as LEC growth crystals, which restricts the utility of the crystals.

Typical dimensions of the semiconductor crystals are 1-6 inches in diameter and 2-30 inches long. The usual rate of crystal growth is 1-5mm per hour. [2]

Cutting, Polishing, and Etching

The bulk crystals (boule) has is generally cylindrical with conical ends, which are usually cut off and wasted because their diameter isn't big enough to be used. Next, the boule is ground to ensure a uniform diameter over the length of the boule which is usually done with a lathe, or similar tool. The crystals need to be aligned using x-ray diffraction and then the boule is cut into wafers. In this process nearly one third of the total mass can be lost due to the width of the cutting mechanism. [2] The sawing also leaves a damaged layer of semiconductor which is etched off. The final step in processing the semiconductor is polishing. There are two different types of waste that are produced during polishing, liquid and solid wastes. The wastewater from GaAs polishing can contain arsenic and gallium waste in concentrations between 200 and 400 ppm. [2]

Thin Film Growth

Thin films of GaAs have many advantages over large single crystals of GaAs when it comes to being used in solar cells. Thin films lack some of the impurities found in large crystals, and are capable of being used without requiring extensive slicing. The rest of the case study will be dedicated to thin film GaAs semiconductors.

The most common thin film growth methods for producing GaAs films are Vapour Phase Epitaxy (VPE), Metalorganic Chemical Vapour Deposition (MOCVD), and Molecular Beam Epitaxy (MBE).


Plausibility of Recycling

Amount of material in a typical cell = 3100 g/m2

Peak Power = 272.8 W/m2

Amount of material per Watt Peak = 11.4 g/Wpeak[3]


Metalorganic Chemical Vapour Deposition (MOCVD)

Material utilization efficiency = 30%[4]

Waste material rate MOCVD = 2170 g/m2 and 7.98 g/Wpeak


Molecular Beam Epitaxy

Material utilization efficiency for Ga = 40-70%

Material utilization efficiency for As = 10-20%

Average Material utilization efficiency = 35%

Waste material rate MBE = 2015 g/m2 and 7.41 g/Wpeak


Forms of Collection of Waste

References

  1. R.L. Adams, Growth of high purity GaAs using low-pressure vapour-phase epitaxy, Nuclear Instruments and Methods in Physics Research Section A: Accelerators, Spectrometers, Detectors and Associated Equipment, Volume 395, Issue 1, 1 August 1997, Pages 125-128, ISSN 0168-9002, 10.1016/S0168-9002(97)00624-4. (http://www.sciencedirect.com/science/article/pii/S0168900297006244) Keywords: Low-pressure vapour-phase epitaxy; LPVPE; GaAs
  2. 2.0 2.1 2.2 Swartzbaugh Joseph, Sturgill Jeffery. Reduction of Arsenic Wastes in the Semiconductor Industry, 1998
  3. http://www.spacequest.com/products/SP-X.pdf
  4. http://www.bnl.gov/pv/files/pdf/art_168.pdf